Corrosion Properties of Ag-Au-Cu-Pd System Alloys Containing Indium
Ag-Au-Cu-Pd system alloy Corrosion resistance Tarnish
2010/12/1
In this study, the corrosion resistance of Ag-Au-Cu-Pd system alloys consisting of 5 or 10 mass% indium was evaluated. Levels of element release and tarnish were determined and electrochemical measure...
Tarnish resistance evaluation of experimental Pd-free Ag-Au-Pt-Cu dental alloys
Dental alloys Tarnish resistance Discoloration
2010/11/29
This study evaluated the tarnish resistance of eight experimental Pd-free Ag-Au-Pt-Cu dental alloys in a 0.1% Na2S aqueous solution at 37°C. Color measurements of the plate samples were made using a c...
This study compared the resistance to removal by traction of abraded cylindrical metal cast posts of Cu-Al (Goldent-LA). The posts had constant length (9 mm) and three different diameters (0.9, 1.3 an...
Sulfuration Resistance of Five Experimental Ag-Pd-Au-Cu Alloys with Low Pd Content of 10 or 12%
Ag-Pd-Au-Cu alloys Low Pd content Sulfuration resistance
2009/9/14
Commercial Ag-based alloy (46Ag-20Pd-12Au-20Cu alloy) is widely used in Japan as a casting alloy. As opposed to the commercial composition, we prepared five experimental Ag-based alloys with reduced P...
Effect of additive metals, Sn, Ga, and In in Ag-Pd-Au-Cu alloys on initial bond strength of 4-META adhesive cement to these alloys
Ag-Pd-Au-Cu Alloy Bond Strength 4-META adhesive cement
2009/9/11
The purpose of this study was to investigate the effects of three additives, Sn, Ga, and In, as well as the main constituents, Pd and Cu, of Ag-Pd-Au-Cu alloys on the initial bond strength of 4-META a...